EN 16482: 2014 | IN GJL-600-3C
GGG-60/3
Available formats: Sheet metal, plates, bars, profiles and wires.
GGG-60 offers reasonable machinability and excellent surface finish combined with an increase in tensile strength and high wear resistance. Responding well to heat treatment compared to Unibar 400-15 and 500-7. It absorbs noise and vibrations well. Complies with Standard EN 16482: 2014 | IN GJS-600-3C
Brinell hardness
210-260 HB with 10 mm diameter ball and 3000Kg load depending on the size of the section. Hardness readings are taken throughout the entire section of the bar. The hardness values for rectangles depend on the relationship between height and width and can be supplied upon request.
Micro structure
It contains nodular (spheroidal) graphite type V & VI according to ISO 945. The perfumery contains approximately 200/250 nodules / mm2 and is predominantly perlitic, with a nucleus containing 90/150 nodules / mm2. The core matrix has more than 50% of perlite with some ferrite). Cold carbides will be less than 5%, well dispersed.
Chemical composition
|
%
|
C
|
Si
|
Mn
|
S
|
P
|
Mg
|
-
|
Others / Alloys
|
Fe
|
|
Min. |
3,25 |
2,4 |
0,1 |
0,005 |
0,015 |
0,04 |
- |
- |
- |
|
Max. |
3,7 |
3 |
0,4 |
0,02 |
0,08 |
0,07 |
- |
Residual |
Balance |
Typical ranges: (Analysis at the discretion of the manufacturer)
features
GGG-60 offers reasonable machinability and excellent surface finish combined with an increase in tensile strength and high wear resistance. Responding well to heat treatment compared to Unibar 400-15 and 500-7. It absorbs noise and vibrations well. Complies with Standard EN 16482: 2014 | IN GJS-600-3C
Brinell hardness
210-260 HB with 10 mm diameter ball and 3000Kg load depending on the size of the section. Hardness readings are taken throughout the entire section of the bar. The hardness values for rectangles depend on the relationship between height and width and can be supplied upon request.
Micro structure
It contains nodular (spheroidal) graphite type V & VI according to ISO 945. The perfumery contains approximately 200/250 nodules / mm2 and is predominantly perlitic, with a nucleus containing 90/150 nodules / mm2. The core matrix has more than 50% of perlite with some ferrite). Cold carbides will be less than 5%, well dispersed.
Chemical composition
|
Element
|
Min.%
|
Max. %
|
|
C Si Mn S P Mg - - - Others / Alloys Fe |
3,25 2,4 0,1 0,005 0,015 0,04 - - - - - |
3,7 3 0,4 0,02 0,08 0,07 - - - Residual Balance |
Typical ranges: (Analysis at the discretion of the manufacturer)
Size range
|
Standard Measures
|
Dimensions and supply
|
|
25mm round? 600mm |
On request |
|
Square 30mm x 30mm? 510mm x 510mm |
On request |
|
Rectangular Up to 750mm x 560mm |
On request |
|
Gross supply of casting, turning, drilling, milling |
Too much machining according to general catalog |
|
Long Length Standard 3 meters |
Custom cut of parts |
General Physical Properties
|
Quality
|
Material Section
|
Tensile strength N / mm2
|
L. Elastic 0.2% N / mm2
|
Elongation%
|
Hardness (HB)
|
Matrix
|
| GGG-60/3 EN 16482: 2014 IN GJL-600-3C | 20 <D? 60 | 600 | 370 | 3 | 210 - 260 | Ferritic Perlitic |
| 60 <D? 120 | 600 | 360 | 2 | |||
| 120 <D? 400 | 550 | 340 | 1 | |||
| 400 <D? 700 | ? 550 * | 340 | 1 |
* By way of indication, specification of agreement between smelter and client.
Physical Properties
| Quality | GGG-60/3 - EN 16482: 2014 - EN GJL-600-3C |
| Material Section | |
| 20 <D? 60 | |
| 60 <D? 120 | |
| 120 <D? 400 | |
| 400 <D? 700 | |
| Expected values of tensile strength N / mm2 | |
| 600 | |
| 600 | |
| 550 | |
| ? 550 * | |
| L. Elastic 0.2% N / mm2 | |
| 370 | |
| 360 | |
| 340 | |
| 340 | |
| Elongation% | |
| 3 | |
| 2 | |
| 1 | |
| 1 | |
| Hardness (HB) | 210 - 260 |
| Matrix | Perlitic Ferritic |
Taken from a half radius of the molten bar, do not test apart from the molten bar.
Formats
- Rectangular Iron Profiles GGG-60/3
- Round Iron Profiles GGG-60/3
- Square Iron Profiles GGG-60/3
- GGG-60/3 Iron Pipes